| 1. Identificação | ||||
| Tipo de Referência | Artigo em Evento (Conference Proceedings) | |||
| Site | mtc-m21b.sid.inpe.br | |||
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S | |||
| Identificador | 8JMKD3MGP3W34P/3KJ9PSL | |||
| Repositório | sid.inpe.br/mtc-m21b/2015/11.11.12.12 (acesso restrito) | |||
| Última Atualização | 2021:01.15.19.41.54 (UTC) simone | |||
| Repositório de Metadados | sid.inpe.br/mtc-m21b/2015/11.11.12.12.41 | |||
| Última Atualização dos Metadados | 2021:01.15.19.41.55 (UTC) simone | |||
| Chave Secundária | INPE--PRE/ | |||
| Chave de Citação | MaruyaFernUedaRamo:2015:PhTrMe | |||
| Título | Phase transformations in mechancially alloyed and sintered Ti-XMg-22Si-11B (X = 2 and 6 at.-%at) powders  | |||
| Ano | 2015 | |||
| Data de Acesso | 21 maio 2024 | |||
| Tipo Secundário | PRE CI | |||
| Número de Arquivos | 1 | |||
| Tamanho | 1102 KiB | |||
| 2. Contextualização | ||||
| Autor | 1 Maruya, L. O. 2 Fernandes, Bruno Bacci 3 Ueda, Mário 4 Ramos, A. S | |||
| Identificador de Curriculo | 1 2 3 8JMKD3MGP5W/3C9JHSB | |||
| Grupo | 1 2 LAP-CTE-INPE-MCTI-GOV-BR 3 LAP-CTE-INPE-MCTI-GOV-BR | |||
| Afiliação | 1 Universidade Federal de Alfenas (UNIFENAS) 2 Instituto Nacional de Pesquisas Espaciais (INPE) 3 Instituto Nacional de Pesquisas Espaciais (INPE) 4 Universidade Federal de Alfenas (UNIFENAS) | |||
| Endereço de e-Mail do Autor | 1 2 bruno.fernandes@inpe.br 3 ueda@plasma.inpe.br | |||
| Nome do Evento | International Latin American Conference on Powder Technology, 10 (PTECH) | |||
| Localização do Evento | Mangaratiba, RJ | |||
| Data | 8-11 Nov. | |||
| Histórico (UTC) | 2015-11-11 12:12:41 :: simone -> administrator :: 2018-06-04 02:55:51 :: administrator -> simone :: 2015 | |||
| 3. Conteúdo e estrutura | ||||
| É a matriz ou uma cópia? | é a matriz | |||
| Estágio do Conteúdo | concluido | |||
| Transferível | 1 | |||
| Tipo do Conteúdo | External Contribution | |||
| Resumo | This work reports on effect of magnesium addition on the Ti6Si2B stability in Ti-xMg-22Si-11B (x = 2 and 7 at.-%) alloys prepared by high-energy ball milling and subsequent sintering. Ball milling was conducted under Ar atmosphere in stainless steel vials and balls. Following, the powders milled for 600 minutes were uniaxially compacted in order to obtain cylinder samples with 6 mm diameter. To obtain the equilibrium structures the green samples were sintered at 1100oc for 240 minutes under Ar atmosphere. X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS) were used to characterize the as-milled powders and sintered samples. XRD patterns of as-milled Ti-7Mg-22Si-11B powders indicated the presence of Ti peaks only, indicating that extended Ti solid solutions were achieved. In contrary, the Ti5Si3 phase was also formed during milling of Ti-2Mg-22Si-11B powders. After sintering at 1100oC for 240 min, both the Ti-2Mg-22Si-11B and Ti-7Mg-22Si-11B alloys indicated the presence of Ti6Si2B phase as matrix. However, the amount of Ti and TiB precipitates was increased in microstructure of the Ti-7Mg-22Si-11B alloy. | |||
| Área | FISPLASMA | |||
| Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAP > Phase transformations in... | |||
| Conteúdo da Pasta doc | acessar | |||
| Conteúdo da Pasta source | não têm arquivos | |||
| Conteúdo da Pasta agreement |
| |||
| 4. Condições de acesso e uso | ||||
| Arquivo Alvo | maruya_phase.pdf | |||
| Grupo de Usuários | simone | |||
| Grupo de Leitores | administrator simone | |||
| Visibilidade | shown | |||
| Permissão de Leitura | deny from all and allow from 150.163 | |||
| Permissão de Atualização | não transferida | |||
| 5. Fontes relacionadas | ||||
| Repositório Espelho | urlib.net/www/2011/03.29.20.55 | |||
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ET2RFS | |||
| Lista de Itens Citando | sid.inpe.br/bibdigital/2013/09.25.21.49 1 sid.inpe.br/mtc-m21/2012/07.13.14.56.06 1 | |||
| Acervo Hospedeiro | sid.inpe.br/mtc-m21b/2013/09.26.14.25.20 | |||
| 6. Notas | ||||
| Campos Vazios | archivingpolicy archivist booktitle callnumber copyholder copyright creatorhistory descriptionlevel dissemination doi e-mailaddress edition editor format isbn issn keywords label language lineage mark nextedition notes numberofvolumes orcid organization pages parameterlist parentrepositories previousedition previouslowerunit progress project publisher publisheraddress rightsholder schedulinginformation secondarydate secondarymark serieseditor session shorttitle sponsor subject tertiarymark tertiarytype type url versiontype volume | |||
| 7. Controle da descrição | ||||
| e-Mail (login) | simone | |||
| atualizar | ||||